Friction Material
For the most demanding applications we have the most advanced solutions.
YARN
Friction material re-inforced with fibers and metal wire which give smooth engagement, very high revolution and wear resistance. For years it has been the standard material for clutch facings. Due to very good friction and mechanical properties it is also used in several industrial applications.
Available in rings, sheets and machined parts, easy to bond.
| NAME | STATIC COEF. (U) | DYNAMIC COEF. (U) | T FADING (ºC) | WEAR RATE (mm3KWH) | COMPRESSIVE STRENGTH (MPa) | |
|---|---|---|---|---|---|---|
| G95 | 0.60±0.05 | 0.55±0.05 | >300 | 25 (at 150 ºC) | 120±5 | |
| JTC | 0.45±0.05 | 0.40±0.05 | >400 | 35( at 150ºC) | 145±5 | |
| HDS57 | 0.53±0.05 | 0.50±0.05 | >350 | 30 (at 150 ºC) | 120±5 | |
| HCC | 0.45±0.05 | 0.45±0.05 | >400 | 35 (at 150 ºC) | 140±5 | |
| VH-03 | 0.44±0.05 | 0.38±0.05 | >350 | 30 (at 150 ºC) | 120±5 | |
| V2000R | 0.46±0.05 | 0.50±0.05 | >350 | 30 (at 150 ºC) | 120±5 |